The effects of aging exposures to three non-saline aqueous environments on the compressive mechanical properties of a calcium carbonate-filled bisphenolic epoxy adhesive, cold-cured with the addition of two curing agents suitable for the cure at ambient temperature (i.e., Mannich base and triethylenetetramine), were assessed. The amount of the added filler (CaCO3) varied from 1 to 3 g per 100 g of resin; the immersion times in each of the selected medium varied from 1 to 10 months. It was found that the mechanical properties measured in compression mode on cylindrical specimens of unfilled and CaCO3 -loaded epoxy were scarcely influenced by the kind of curing agent employed; only the compressive modulus was limitedly affected by this parameter. Referring to the behavior when aged in water, the CaCO3 -filled epoxies displayed noticeable growths in modulus, small reductions in strength, and limited variations in strain, with a certain influence of the exposure time, especially when comparing the properties at the lowest time with those at medium–long times. On the basis of the results of statistical MANOVA analysis, it can be concluded that among the compositional factors (i.e., the type of curing agent employed to cure the epoxy compounds and the micro-filler content), only the amount of CaCO3 filler significantly affects the compressive modulus.

Cold-Cured Bisphenolic Epoxy Adhesive Filled with Low Amounts of {CaCO}3: Effect of the Filler on the Durability to Aqueous Environments

Mariaenrica Frigione
2021-01-01

Abstract

The effects of aging exposures to three non-saline aqueous environments on the compressive mechanical properties of a calcium carbonate-filled bisphenolic epoxy adhesive, cold-cured with the addition of two curing agents suitable for the cure at ambient temperature (i.e., Mannich base and triethylenetetramine), were assessed. The amount of the added filler (CaCO3) varied from 1 to 3 g per 100 g of resin; the immersion times in each of the selected medium varied from 1 to 10 months. It was found that the mechanical properties measured in compression mode on cylindrical specimens of unfilled and CaCO3 -loaded epoxy were scarcely influenced by the kind of curing agent employed; only the compressive modulus was limitedly affected by this parameter. Referring to the behavior when aged in water, the CaCO3 -filled epoxies displayed noticeable growths in modulus, small reductions in strength, and limited variations in strain, with a certain influence of the exposure time, especially when comparing the properties at the lowest time with those at medium–long times. On the basis of the results of statistical MANOVA analysis, it can be concluded that among the compositional factors (i.e., the type of curing agent employed to cure the epoxy compounds and the micro-filler content), only the amount of CaCO3 filler significantly affects the compressive modulus.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11587/451702
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 12
  • ???jsp.display-item.citation.isi??? 10
social impact