Al x CoCrCuFeNi high entropy alloys were synthesised through mechanical alloying and spark plasma sintering. Different alloys were produced by varying the aluminium content (x = 0.5, 1.5, 2.5 and 4). The influence of the milling duration on the evolution of microstructure, constituent phases and morphology was studied. Milling time increasing resulted in grain refinement and higher solid solution homogenisation characterised by a high internal strain. As a consequence of aluminium addition, the materials’ microstructure evolved from FCC and BCC phases to FCC, BCC and ordered BCC phases. Both mechanical alloying and SPS conditions as well as aluminium content let to grain refinement and mechanical properties variations. In particular, hardness increased with increasing the aluminium content. The aluminium percentage and the consequent phases evolution is responsible for the microstructural stability at high temperatures.

Crystal structure evolution in mehcanical alloying and spark plasma sintering of AlxCoCrCuFeNi HEAs

Sadeghi B.;Cavaliere P.
2021-01-01

Abstract

Al x CoCrCuFeNi high entropy alloys were synthesised through mechanical alloying and spark plasma sintering. Different alloys were produced by varying the aluminium content (x = 0.5, 1.5, 2.5 and 4). The influence of the milling duration on the evolution of microstructure, constituent phases and morphology was studied. Milling time increasing resulted in grain refinement and higher solid solution homogenisation characterised by a high internal strain. As a consequence of aluminium addition, the materials’ microstructure evolved from FCC and BCC phases to FCC, BCC and ordered BCC phases. Both mechanical alloying and SPS conditions as well as aluminium content let to grain refinement and mechanical properties variations. In particular, hardness increased with increasing the aluminium content. The aluminium percentage and the consequent phases evolution is responsible for the microstructural stability at high temperatures.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11587/447942
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 4
  • ???jsp.display-item.citation.isi??? ND
social impact