This study reports the effect of three new titanium phosphates Li0.5M0.25Ti2(PO4)3 (where M = Mn, Co and Ni) on the protective properties of alkyd resin films applied on carbon steel substrate in 3.5% sodium chloride solution. The performance of the coatings was evaluated by electrochemical impedance spectroscopy, oxygen and water permeability and pull-off adhesion measurements. It was found that titanium phosphates improve the corrosion resistance as well as the adhesion strength of alkyd resin coatings. The incorporation of titanium phosphates into the alkyd resin coating significantly enhances the pore resistance of the alkyd resin and decreases the coating capacitance. Lower water and oxygen permeability were observed for alkyd resin containing titanium phosphates, confirming formation of a protective layer on the surface. The order of anticorrosion performance of the three coatings was as follows: Li0.5Mn0.25Ti2(PO4)3 > Li0.5Co0.25Ti2(PO4)3 > Li0.5Ni0.25Ti2(PO4)3.

Influence of newly synthesized titanium phosphates on the corrosion protection properties of alkyd coating

DE RICCARDIS, ALBERTO;MELE, Giuseppe Agostino
2016

Abstract

This study reports the effect of three new titanium phosphates Li0.5M0.25Ti2(PO4)3 (where M = Mn, Co and Ni) on the protective properties of alkyd resin films applied on carbon steel substrate in 3.5% sodium chloride solution. The performance of the coatings was evaluated by electrochemical impedance spectroscopy, oxygen and water permeability and pull-off adhesion measurements. It was found that titanium phosphates improve the corrosion resistance as well as the adhesion strength of alkyd resin coatings. The incorporation of titanium phosphates into the alkyd resin coating significantly enhances the pore resistance of the alkyd resin and decreases the coating capacitance. Lower water and oxygen permeability were observed for alkyd resin containing titanium phosphates, confirming formation of a protective layer on the surface. The order of anticorrosion performance of the three coatings was as follows: Li0.5Mn0.25Ti2(PO4)3 > Li0.5Co0.25Ti2(PO4)3 > Li0.5Ni0.25Ti2(PO4)3.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11587/408936
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 50
  • ???jsp.display-item.citation.isi??? 48
social impact