The authors report on the blue electroluminescence from CdSe/ZnS core/shell nanocrystals prepared from ultrasmall, magic size CdSe clusters that have a diameter of less than 2 nm. The light emitting device consists of an active layer of nanocrystals blended with 4,4('),N,N-'- diphenylcarbazole and an evaporated electron transporting/hole blocking layer made of 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline. A blue, stable electroluminescence at 485 nm from the hybrid device was observed, in good agreement with the photoluminescence spectra of a solid film of the same nanocrystals used for the device. (c) 2007 American Institute of Physics.
Blue light emitting diodes based on fluorescent CdSe/ZnS nanocrystals
GIGLI, Giuseppe
2007-01-01
Abstract
The authors report on the blue electroluminescence from CdSe/ZnS core/shell nanocrystals prepared from ultrasmall, magic size CdSe clusters that have a diameter of less than 2 nm. The light emitting device consists of an active layer of nanocrystals blended with 4,4('),N,N-'- diphenylcarbazole and an evaporated electron transporting/hole blocking layer made of 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline. A blue, stable electroluminescence at 485 nm from the hybrid device was observed, in good agreement with the photoluminescence spectra of a solid film of the same nanocrystals used for the device. (c) 2007 American Institute of Physics.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.