Two-dimensional electron gas (2DEG) transport in Al0.3Ga0.7N/AlN/GaN heterostructures has been studied using magnetic-field dependent Hall-effect measurements and advanced mobility spectrum analysis techniques over the temperature range from 95 K to 300 K. It is shown that electronic transport is due to a single well-defined 2DEG species, with room-temperature sheet concentration and average mobility of 9.3×1012 cm-2 and 1,880 cm2/Vs, respectively. No parasitic conduction through the bulk GaN layer was detected. Importantly, it is shown that the 2DEG exhibits an approximately Gaussian mobility distribution, the linewidth of which broadens with increasing temperature. This is the first reported observation of thermal broadening effects in the 2DEG mobility distribution.

Thermal broadening of two-dimensional electron gas mobility distribution in AlGaN/AlN/GaN heterostructures

DE VITTORIO, Massimo;
2010-01-01

Abstract

Two-dimensional electron gas (2DEG) transport in Al0.3Ga0.7N/AlN/GaN heterostructures has been studied using magnetic-field dependent Hall-effect measurements and advanced mobility spectrum analysis techniques over the temperature range from 95 K to 300 K. It is shown that electronic transport is due to a single well-defined 2DEG species, with room-temperature sheet concentration and average mobility of 9.3×1012 cm-2 and 1,880 cm2/Vs, respectively. No parasitic conduction through the bulk GaN layer was detected. Importantly, it is shown that the 2DEG exhibits an approximately Gaussian mobility distribution, the linewidth of which broadens with increasing temperature. This is the first reported observation of thermal broadening effects in the 2DEG mobility distribution.
2010
9781424466580
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11587/365845
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact