A highly porous (~90%) interconnected hydroxyapatite/wollastonite (HA/WS) scaffolds were prepared by polymeric sponge replica method using a slurry containing HA:Calcium silicate in the weight ratio of 50:50 and sintered at 1300 oC. The phase purity of the scaffolds were analyzed by using XRD. The pore size, pore structure, microstructure and elemental analysis of the scaffolds before and after SBF soaking were analyzed using SEM and EDS. In-vitro bioactivity and bioresorbability confirmed the feasibility of the developed scaffolds. The HA/WS scaffold shows two fold increase in the compressive strength compared to pure HA scaffold.

Mechanical Performance and In Vitro Studies of Hydroxyapatite/Wollastonite Scaffold for Bone Tissue Engineering

KUNJALUKKAL PADMANABHAN, SANOSH;CARROZZO, MARINA;GERVASO, FRANCESCA;SCALERA, FRANCESCA;SANNINO, Alessandro;LICCIULLI, ANTONIO ALESSANDRO
2012-01-01

Abstract

A highly porous (~90%) interconnected hydroxyapatite/wollastonite (HA/WS) scaffolds were prepared by polymeric sponge replica method using a slurry containing HA:Calcium silicate in the weight ratio of 50:50 and sintered at 1300 oC. The phase purity of the scaffolds were analyzed by using XRD. The pore size, pore structure, microstructure and elemental analysis of the scaffolds before and after SBF soaking were analyzed using SEM and EDS. In-vitro bioactivity and bioresorbability confirmed the feasibility of the developed scaffolds. The HA/WS scaffold shows two fold increase in the compressive strength compared to pure HA scaffold.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11587/362358
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 1
  • ???jsp.display-item.citation.isi??? ND
social impact