A simple sol-gel precipitation technique to synthesize nano hydroxyapatite (HA) particles (∼30 nm) that show similar morphology, size and crystallinity to HA crystals of human teeth is reported. Calcium nitrate tetrahydrate and potassium dihydrogenphosphate were used as calcium and phosphorus precursors, respectively. Double distilled water was used as a diluting media for HA sol preparation and ammonia was used to adjust the pH to 11. After aging, the HA gel was dried at 40 °C and calcined to different temperatures ranging from 200 to 600 °C. The dried and calcined powders were characterized for phase composition using X-ray diffractrometry, and Fourier transform infra-red spectroscopy. The particle size and morphology was studied using Transmission electron microscopy. The particle size distribution analysis of HA powders showed skewed distribution plot. The phase and particle characterization studied above showed that HA calcined at 600 °C simulate HA crystals of teeth. © 2009 Elsevier B.V. All rights reserved.

Synthesis of nano hydroxyapatite powder that simulate teeth particle morphology and composition

Sanosh K. P.;
2009-01-01

Abstract

A simple sol-gel precipitation technique to synthesize nano hydroxyapatite (HA) particles (∼30 nm) that show similar morphology, size and crystallinity to HA crystals of human teeth is reported. Calcium nitrate tetrahydrate and potassium dihydrogenphosphate were used as calcium and phosphorus precursors, respectively. Double distilled water was used as a diluting media for HA sol preparation and ammonia was used to adjust the pH to 11. After aging, the HA gel was dried at 40 °C and calcined to different temperatures ranging from 200 to 600 °C. The dried and calcined powders were characterized for phase composition using X-ray diffractrometry, and Fourier transform infra-red spectroscopy. The particle size and morphology was studied using Transmission electron microscopy. The particle size distribution analysis of HA powders showed skewed distribution plot. The phase and particle characterization studied above showed that HA calcined at 600 °C simulate HA crystals of teeth. © 2009 Elsevier B.V. All rights reserved.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11587/452787
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 140
  • ???jsp.display-item.citation.isi??? 128
social impact