In the present paper, the mechanical properties and the scratch failure mechanisms of Ni–P electroless coatings are described. The material microstructure was studied in as-deposited and annealed conditions through SEM and EDS analyses. Nanoindentation measurements on the coatings showed a remarkable hardening due to the crystallization and precipitation behaviour produced by annealing. The scratch tests, conducted by increasing the load during scratch, revealed the coating failure mechanisms in a broad range of applied stresses up to delamination.

Nanoindentation and scratch behaviour of Ni–P electroless coatings

Cavaliere P.;
2020-01-01

Abstract

In the present paper, the mechanical properties and the scratch failure mechanisms of Ni–P electroless coatings are described. The material microstructure was studied in as-deposited and annealed conditions through SEM and EDS analyses. Nanoindentation measurements on the coatings showed a remarkable hardening due to the crystallization and precipitation behaviour produced by annealing. The scratch tests, conducted by increasing the load during scratch, revealed the coating failure mechanisms in a broad range of applied stresses up to delamination.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11587/435213
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 10
  • ???jsp.display-item.citation.isi??? 9
social impact