Metal halide perovskites are currently emerging as highly promising optoelectronic materials. It has been recently demonstrated that fully inorganic solution processed CsPbBr3 perovskite thin films show good electroluminescence properties combined with high thermal stability. In this work, we investigate in details the amplified spontaneous emission (ASE) properties of CsPbBr3 perovskite thin films, as a function of the temperature and the trap density, modified by changing the CsBr-PbBr2 precursor concentration. ASE is observed in samples from both CsBr-rich solution (low trap density) and equimolar solution (higher trap density), up to about 150 K, with a minimum threshold of 26 and 29 mu J cm(-2) at 10 K, respectively. However, the different distribution of defect states, mainly above the first exciton level in the former and below it in the latter, strongly improved optical gain at 10 K and changed the ASE temperature dependence of CsBr-rich films

Amplified Spontaneous Emission Properties of Solution Processed CsPbBr3 Perovskite Thin Films

De Giorgi, Maria Luisa;Perulli, Andrea;Anni, Marco
2017-01-01

Abstract

Metal halide perovskites are currently emerging as highly promising optoelectronic materials. It has been recently demonstrated that fully inorganic solution processed CsPbBr3 perovskite thin films show good electroluminescence properties combined with high thermal stability. In this work, we investigate in details the amplified spontaneous emission (ASE) properties of CsPbBr3 perovskite thin films, as a function of the temperature and the trap density, modified by changing the CsBr-PbBr2 precursor concentration. ASE is observed in samples from both CsBr-rich solution (low trap density) and equimolar solution (higher trap density), up to about 150 K, with a minimum threshold of 26 and 29 mu J cm(-2) at 10 K, respectively. However, the different distribution of defect states, mainly above the first exciton level in the former and below it in the latter, strongly improved optical gain at 10 K and changed the ASE temperature dependence of CsBr-rich films
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11587/414721
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 60
  • ???jsp.display-item.citation.isi??? 56
social impact