Schottky barrier diodes, on both Ga and N faces of a ∼300-μm-thick free-standing GaN layer, grown by hydride vapor phase epitaxy (HVPE) on Al2O3 followed by laser separation, were studied by capacitance–voltage and deep level transient spectroscopy (DLTS) measurements. From a 1/C2 vs V analysis, the barrier heights of Ni/Au Schottky contacts were determined to be different for the two polar faces: 1.27 eV for the Ga face, and 0.75 eV for the N face. In addition to the four common DLTS traps observed previously in other epitaxial GaN including HVPE-grown GaN a new trap B′ with activation energy ET = 0.53 eV was found in the Ga-face sample. Also, trap E1 (ET = 0.18 eV), believed to be related to the N vacancy, was found in the N-face sample, and trap C (ET = 0.35 eV) was in the Ga-face sample. Trap C may have arisen from reactive-ion-etching damage.

Deep centers in a free-standing GaN layer

VISCONTI, Paolo;
2001-01-01

Abstract

Schottky barrier diodes, on both Ga and N faces of a ∼300-μm-thick free-standing GaN layer, grown by hydride vapor phase epitaxy (HVPE) on Al2O3 followed by laser separation, were studied by capacitance–voltage and deep level transient spectroscopy (DLTS) measurements. From a 1/C2 vs V analysis, the barrier heights of Ni/Au Schottky contacts were determined to be different for the two polar faces: 1.27 eV for the Ga face, and 0.75 eV for the N face. In addition to the four common DLTS traps observed previously in other epitaxial GaN including HVPE-grown GaN a new trap B′ with activation energy ET = 0.53 eV was found in the Ga-face sample. Also, trap E1 (ET = 0.18 eV), believed to be related to the N vacancy, was found in the N-face sample, and trap C (ET = 0.35 eV) was in the Ga-face sample. Trap C may have arisen from reactive-ion-etching damage.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11587/107341
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 102
  • ???jsp.display-item.citation.isi??? 95
social impact